Detailed Notes to Welding Inspection of Welded Steel Pipe
Date:2017-04-19      View(s):1665      Tag:welding inspection, welded steel pipe, welded carbon steel pipe
The contents of the welded steel pipe welding inspection include the inspection of the materials, tools, equipment used in the whole production process, process and finished product from drawing design to product completed. It is divided into three stages: pre-weld inspection, inspection in welding process, finished product inspection after welding. According to whether damage the welded carbon steel pipe or not, test methods can be divided into destructive testing and non-destructive testing two categories. Next, Prime Steel Pipe will provide all for everyone.


Pre-weld inspection


Pre-weld inspection includes the inspection of raw materials (such as base metal, electrodes, flux, etc.) and the inspection of welding structure design.


Inspection in welding process


Inspection in welding process includes the inspection of welding process specifications, the inspection of weld size, the inspection of fixture conditions and structural assembly quality.


Finished product inspection after welding


There are many methods of finished product inspection after welding, commonly used are the following:


No 1. Appearance inspection


The appearance inspection of the welded joint is a inspection method with simple procedure, but it is widely used, and it is an important part of the finished product inspection. It is mainly used to find the defect on the surface of welded steel pipe weld seam and the size of the deviation. We generally observe through the naked eye, or testing by virtue of the standard model, gauge and magnifying glass and other tools. If there is a defect on the surface of the weld seam, it is possible that there is a defect in the weld.


No 2. Confidentiality testing


The defects of brazing joints of welded seam of welded vessel for the temporarystorage of a gas orliquid, such as perfoliate cracks, porosity, slag inclusion, incomplete fusion and loose organization, etc. can be found by compactness test. Compactness test includes kerosene test, water-bearing test, hose test, etc.


No 3. Strength test of the pressure vessel


Except carrying out encapsulation test, we also should carry out strength test to pressure vessel. Two kinds of methods are commonly, hydraulic pressure test and air pressure test. Each of them can test the welded seam compactness of vessel and pipe working under pressure. Pneumatic tests are more sensitive and rapid than hydrostatic tests, the tested products need not to drain off water,it is particularly suitable for difficult drainage products. But the risk of testing is bigger than the hydraulic test. During the test, the corresponding safety and technical measures must be observed to prevent accidents during the test.


No 4. Physical inspection method


Physical inspection method is a method that using some physical phenomena to measure or test. the inspection of materials or parts of the internal defects, generally use non-destructive testing methods. Currently, non-destructive testing includes ultrasonic testing, ray detection, penetration testing, magnetic detection and so on.


① Ray detection


Ray detection is a detection method that use the characteristics of ray can penetrate the material and has attenuation in the material to find defects. Ray inspection is mainly used to test the cracks inside the weld, incomplete penetration, porosity, slag and other defects.


② Ultrasonic testing


Ultrasound can spread in the metal and other uniform media, due to it will produce reflection in the interface of different media, it can be used for testing internal defects. Ultrasonic can test the defect of any welding material and on any part, and it can be more sensitive to find the location of defects. But the nature of defects, shape and size is more difficult to determine. So ultrasonic testing often used in conjunction with the ray test.


③ Magnaflux inspection


Magnaflux inspection is a detection method that use the leakage of magnetic produced by magnetic field, magnetized iron, magnetic metal parts to find defects. According to different methods of magnetic flux leakage, it can be divided into magnetic powder, magnetic induction and magnetic recording method, magnetic powder is the most widely use method. Magnetic flaw detection can only discover the defect on the surface or the near surface of the magnetic metal.


④ Penetration testing


Permeability testing uses certain liquids such as the permeability of the physical properties to find and display defects, including color inspection and fluorescence detection It can be used to check the defect on the surface of ferromagnetic and non-ferromagnetic material.